Corrosion resistance, anti-fouling, high-strength.
Housings, pump and valve bodies, impellers, bushings, low-duty gears, trunnions, brackets, bearing blocks, especially where corrosion resistance is an advantage.
|CAST (reference)||SPEE3D PRINTED||WROUGHT (reference)|
|Standard||C85400 Brass spec3||Aluminium Bronze as heat treated4||CW305G spec5|
|Yield Strength (MPa)||ASTM E82||76||160 (min)||180|
|Ultimate Tensile Strength (MPa)||ASTM E82||207||300 (min)||420|
|Elongation at break (%)||ASTM E82||20||8 (min)||20|
|Hardness Brinell (HB)||ASTM E18||45||87 (typ)||100|
1.Properties shown reflect beta processing parameters. Properties were obtained for heat treatment loads between 0.2 kg and 3 kg.
2.Specimens tested according to ASTM E8.
3.From ASTM standard B271.
4.Samples were heat treated according to SPEE3D’s standard operating procedure.
5.From standard EN 12165:1998.
Listed designations are for reference purposes only. Composition and mechanical properties may vary. End-use material performance is impacted (+/-) by certain factors including but not limited to part geometry and design, application and evaluation conditions.