410 Stainless Steel
Características de los materiales
Acceptable machineability, moderate corrosion resistance, good ductility, medium strength
Aplicaciones
Couplings and adaptors, shaft flanges, stub axles, bushings, actuator arms, low-speed cam followers, medium duty gears, conveyors, rails, fixtures, brackets, housings, especially where 316L stainless falls short on strength or wear resistance.
| Elemento | Porcentaje |
|---|---|
| Fe | Bal |
| C | < 0.05% |
| Si | < 0.65-0.9% |
| Cr | < 11.5-13% |
| Mn | < 0.15-0.45% |
| S | < 0.3% |
| CAST | SPEE3D IMPRESO | WROUGHT | |
| (reference) (ASTM A743 CA15, to ASTM A487 Class D) | 410 Stainless Steel | (reference)(EN10088-3 1.4006 QT650) | |
| Límite elástico (MPa)1 XY,Z | 515 | 515 | 480 |
| Resistencia a la tracción (MPa)1 XY,Z | 690 | 645 | 720 |
| Alargamiento a la rotura (min %)1 XY,Z | 17 | 10 | 20 |
| Dureza Vicker (HV)2 XY,Z | 185-255 | 201-218 | 190-230 |
| Índice de corrosión (mmpy) | N/A | N/A | N/A |
Información ASTM:
- Specimens tested according to ASTM E8 Subsize Specimens.
- De ASTM E92-17 Standard Test Methods for Vickers Hardness and Knoop Hardness of Metallic Materials.
Las designaciones que figuran en la lista son sólo de referencia. La composición y las propiedades mecánicas pueden variar. El rendimiento del material en su uso final se ve afectado (+/-) por determinados factores, entre los que se incluyen la geometría y el diseño de la pieza, la aplicación y las condiciones de evaluación.
Abreviaturas:
XY = La dirección XY se define como la dirección a lo largo de una capa de impresión.
Z = La dirección Z se define como la dirección perpendicular a la capa de impresión, normal al plano XY.